Getting a TIG welder and need some advice please

**cropwell** · 08-11-2015

I am thinking about getting a TIG welder and need some advice.

The frame I will be building is 5mm thick section, so the first question is - What power welder do I need ?

Is this one suitable ? It is in my price range http://welduk.com/product/sip-05266-...-torch-160-amp AND WeldUK deal with welding equipment and not much else. I have bought from them before and I trust them. I say this because the cheaper 200A welders on eBay all seem to be sold by businesses that sell all sorts of fancy goods and have low feedback scores.

What does the team think ?

Rob

**Web Goblin** · 09-11-2015

I like the advert. Very high duty cycle @60%. I think not!
You will be low on current at 160 amps for 5mm thick. I think you would need around 200-220 amps.
Why tig? Why not MMA?

**komatias** · 09-11-2015

With a TIG welder you will be able to do MMA (stick) they, just need to swap polarities. MMA's are cheap as chips nowdays.

When I was looking for a welder, I wanted something that would do AC as well, mostly because I wanted to do aluminium. The price does go up though. In the end I went with the R-Tech 161 as I could pick it up from close to the office and they had shop soiled items at a discount compared to new.

**cropwell** · 09-11-2015

Originally Posted by komatias

When I was looking for a welder, I wanted something that would do AC as well, mostly because I wanted to do aluminium.

That's a good point about ali, I was wondering why this one stated welds steel and copper. Thanks for highlighting that.

How about this machine and supplier http://www.ebay.co.uk/itm/AC-DC-TIG-...EAAOSwDk5Tz618 anybody got any experience of this seller ?

Rob

**JAZZCNC** · 09-11-2015

Tig is nice but only if you want to weld materials that have heat considerations like Stainless, Ti, Ali etc or thin materials. Also To weld Ali and other exotics requires much more expensive gases like Pure Argon or Argon & helium mix etc so unless you have need for cosmetic welds and thin heat sensitive materials then for the run of mill steels then much quicker and cheaper with MIG.

Then you have the learning curve which is much higher than MIG or MMA esp when you talking Ali etc. You'll use much more consumables with TIG when learning because just the slightest touch down of the tip means stopping and redressing the tungston otherwise your always going to struggle.

Also Don't buy a Cheap Tig if you plan on welding Ali or more exotic material or thin material and cosmetic welds etc because you need the flexabilty of the settings and they are often limited.

For 5mm steel I'd go MMA for the cheapest option or Big Mig with decent duty cycle.

**cropwell** · 09-11-2015

Well now it looks like I can't afford anything for a while. I had to buy a new office printer after the old colour laser 'refused to cooperate'. I shall be taking it for an extended holiday at the recycling centre !

I have a reasonable Mig machine, so I can live with that, but Tig would have been a nice toy. I have learned a lot about Tig in the past couple of days though.

Cheers

Rob

**cropwell** · 09-11-2015

Originally Posted by Web Goblin

I like the advert. Very high duty cycle @60%. I think not!
You will be low on current at 160 amps for 5mm thick. I think you would need around 200-220 amps.
Why tig? Why not MMA?

The WeldUK advert is just lifted from the SIP site, so they say 60%

I think I could multipass weld 5mm OK

Rob

**sambo2** · 08-07-2016

Sorry for the thread resurrection Rob. I read it as the last post was 13 hours ago but that was the last time you were online.. oops.
Do you mind sharing your gas supplier? Mine is just sitting there most of the time too. I haven't used it for a year now, I only remembered I still had it when boc invoiced me haha.