Dunno what you mean...

Actually, the stuff does shrink somewhathaving thought about it as I have seen cracks in large pours - no getting away from it when it's mixed so as to be pourable I guessbut I bet if you mixed it dry enough it would be reduced to a minimum. If you cast it into a steel form why would it not be good enough to fix rails to it directly?