Thor, or should that be Zeus?

[JAZZCNC]

Lol. Ye, the 52.5R stuff is whiter than the white we are typing on here ....

Probably why it's called SNOW Crete then. . Lol

[Chaz]

Probably why it's called SNOW Crete then. . Lol

Id guess its related. Its used extensively for architectural concrete work.

[Chaz]

Some progress. Have removed some of the wood to see. Nice clean finish, no air bubbles (as expected with the plastisizer). Struggling to get the wood out, even with a mold release agent, its too tight to come out.


I need some advice on sizing some metal. I want to build a frame below the concrete to hold the mass and allow some castor wheels to be mounted. Estimated weight will be 2000kg when done. Can anyone suggest what size mild steel tube I can use?


Thanks

[Fenza]

You could always build the frame out of UHPC as well. Just a thought

What happened to that rod in the first photo?

Fenza

[Chaz]

You could always build the frame out of UHPC as well. Just a thought

What happened to that rod in the first photo?

Fenza

I could but I think its easier to weld something up quickly.

The rod was some material that went into a pipe I was trying to use for a hole in the mould. It moved and filled with concrete, so thought that Id cut it open and inspect (once it had dried).

[Boyan Silyavski]

If it was me i would use 100x100x4 and make a pallet from it. For me this is the ideal profile big enough, easy to cut at home, strong enough, cheap enough, ... . however reinforcing plates where the wheels are.

[Chaz]

Just need to drill some holes into the bearing holder, quick test fit. Have bought some reference surfaces (surface plate for the table) and also a fairly large box (engineering type, flat within 5 thou) that Ill use to cast the DWH against. I was going to try something cheaper but its risky and this will be better.